Physical Properties
|
Metric
|
Comments
|
| Specific Gravity |
1.16 g/cc |
ASTM D792 |
| Water Absorption |
0.6 % |
Immersion, 24hr; ASTM D570(2) |
| Water Absorption at Saturation |
80 |
ASTM D785 |
| Hardness, Rockwell R |
110 |
ASTM D785 |
| Hardness, Shore D |
75-80 |
ASTM D2240 |
| Tensile Strength, Ultimate |
75.8 MPa |
ASTM D638 |
| Elongation at Break |
30 % |
ASTM D638 |
| Tensile Modulus |
2.76 GPa |
ASTM D638 |
| Flexural Modulus |
3.45 GPa |
ASTM D790 |
| Flexural Yield Strength |
110 MPa |
ASTM D790 |
| Compressive Strength |
96.5 MPa |
10% Def.; ASTM D695 |
| Compressive Modulus |
2.76 GPa |
ASTM D695 |
| Shear Strength |
72.4 MPa |
ASTM D732 |
| CTE, linear 68°F |
90 μm/m-°C |
(-40°F to 300°F); ASTM E831 |
| Melting Point |
216 °C |
Crystalline, Peak; ASTM D3418 |
| Maximum Service Temperature, Air |
93.3 °C |
Long Term |
| Deflection Temperature at 1.8 MPa (264 psi) |
93.3 °C |
ASTM D648 |
| Flammability, UL94 (Estimated Rating) |
HB |
1/8 inch |